Quantifying microscale drivers for fatigue failure via coupled ...

Quantifying microscale drivers for fatigue failure via coupled ... - Nature

However, a deterministic failure criteria, which by necessity would involve the sub-surface, 3D microstructure (where many failures occur, ...

Quantifying microscale drivers for fatigue failure via coupled synchrotron. X-ray characterization and simulations. 1School of Aeronautics and Astronautics ...

(PDF) Quantifying microscale drivers for fatigue failure via coupled ...

Fundamentally, knowledge of the strain field around defects during operation and failure is not only of importance for understanding the fracture of nanoscale ...

Quantifying microscale drivers for fatigue failure via coupled ...

Quantifying microscale drivers for fatigue failure via coupled synchrotron. X-ray characterization and simulations. Sven Gustafson1, Wolfgang Ludwig2,3, Paul ...

[PDF] Quantifying microscale drivers for fatigue failure via coupled ...

The authors show unusually large stress gradients near a twin boundary, using X-ray techniques and modelling, which quantify the extreme sub-grain scale ...

Quantifying microscale drivers for fatigue failure via coupled ...

Quantifying microscale drivers for fatigue failure via coupled synchrotron X-ray characterization and simulations. Sven Gustafson, Purdue University. slide.

Quantifying microscale drivers for fatigue failure via coupled ...

Quantifying microscale drivers for fatigue failure via coupled synchrotron X-ray characterization and simulations. Citation Details. Title ...

Quantifying microscale drivers for fatigue failure via coupled ...

Dive into the research topics of 'Quantifying microscale drivers for fatigue failure via coupled synchrotron X-ray characterization and simulations'. Together ...

Quantifying microscale drivers for fatigue failure via coupled ... - OUCI

Quantifying microscale drivers for fatigue failure via coupled synchrotron X-ray characterization and simulations ... Authors: Sven Gustafson; Wolfgang Ludwig ...

Quantification of microscale factors for fatigue failure in NiTi shape ...

Fatigue failure, marked by crack initiation and growth, is intricately linked to microstructural evolution during cyclic loading [4], [5], [6], [7], [8], ...

BlackPhysicists on X: "Quantifying microscale drivers for fatigue ...

Quantifying microscale drivers for fatigue failure via coupled synchrotron X-ray characterization and simulations https://t.co/uiHEmSL3ek.

X-rays quantify stress gradients at twin boundaries, which can drive ...

... quantify the stress ... Quantifying microscale drivers for fatigue failure via coupled synchrotron X-ray characterization and simulations.

Investigation of the Fatigue of Metals by X-ray Scattering - Nature

... fatigue damage ... Quantifying microscale drivers for fatigue failure via coupled synchrotron X-ray characterization and simulations.

‪Darren C. Pagan‬ - ‪Google Scholar‬

2014. Quantifying microscale drivers for fatigue failure via coupled synchrotron X-ray characterization and simulations. S Gustafson, W Ludwig, P Shade, D ...

Automated High‐Throughput Fatigue Testing of Freestanding Thin ...

Fracture, Fatigue, Failure and Damage ... Quantifying microscale drivers for fatigue failure via coupled synchrotron X-ray characterization and ...

Document is current - Crossmark - Crossref

Any future updates will be listed below. Quantifying microscale drivers for fatigue failure via coupled synchrotron X-ray characterization and ...

X-ray microbeam and recrystallization studies of plastic deformation ...

Quantifying microscale drivers for fatigue failure via coupled synchrotron X-ray characterization and simulations. Article Open access 24 June 2020. Explore ...

Evaluating fatigue onset in metallic materials: Problem, current focus ...

It is acknowledged that more than 80 % of failures of metallic structures or materials result from fatigue effects [18], which refer to the progressive damage ...

Quantification of microscale factors for fatigue failure in NiTi shape ...

However, the quantification of microstructural defects associated with fatigue damage of NiTi shape memory alloys. (SMAs) is lacking, which ...

(PDF) Bringing to Life a Newly Discovered Signature of Fatigue ...

... linked to intragrain misorientation, which can be quantified through single grain orientation distributions. ... fatigue failure. In this study, we present a ...