Thermomechanical fatigue crack growth in a single crystal nickel ...

Single crystal nickel base superalloys are frequently used for gas turbine blades due to their excellent ability to withstand high mechanical loads in ...

Thermomechanical fatigue crack growth in a single crystal nickel base superalloy was studied. Tests were performed on single edge notched specimens.

Characterization-and-modeling-of-thermo-mechanical-fatigue-crack ...

Two different fundamental crack growth mechanisms have been identified for the single crystal nickel base superalloy CMSX-2 for five different. Page 56. 36.

Crack growth in single crystal nickel base superalloys under ... - DiVA

Fatigue crack growth testing has been performed, both using conventional isothermal testing methods and also using thermomechanical fatigue ...

[PDF] Crack growth in single crystal nickel base superalloys under ...

This work concerns the fatigue crack growth behaviour of nickel base single crystal superalloys. The main industrial application of this class of materials ...

Thermomechanical fatigue crack growth in a single crystal nickel ...

Thermomechanical fatigue crack growth in a single crystal nickel base superalloy. https://doi.org/10.1016/j.ijfatigue.2019.01.014 ·. Journal: International ...

Coating Effects on Crack Growth in a Single Crystal Nickel Based ...

Coating Effects on Crack Growth in a Single Crystal Nickel Based Alloy During Thermo-Hechanical Fatigue ... Single Crystal During Thermomechanical Fatigue.

Fatigue crack growth behavior of a new single crystal nickel-based ...

Mughrabi, Aspects of High-Tempera- ture Low-Cycle Thermo-Mechanical Fatigue of a Single Crystal Nickel-base Superalloy,Fatigue and Fracture of Eng. Math ...

Pore-induced defects during thermo-mechanical fatigue of a fourth ...

... thermomechanical fatigue crack growth. Int ... fracture in nickel-base single-crystal superalloys during thermomechanical fatigue cycling.

Coating Effects on Crack Growth in a Single Crystal Nickel Based ...

... Crack Growth in a Single Crystal Nickel Based Alloy During Thermo-Hechanical Fatigue. Source. Single crystal specimens of the nickel based ...

(Open Access) Thermomechanical fatigue crack growth in a single ...

Thermomechanical fatigue crack growth in a single crystal nickel base superalloy was studied.. Dissolution of γ′ precipitates and recrystallization at the ...

(PDF) Thermomechanical fatigue crack growth in a single crystal ...

The performance of the experimental method is demonstrated with trials on an advanced nickel-based superalloy, RR1000. To reduce future testing requirements, ...

16 : Fatigue crack growth rate plot of short thermomechanical cracks

Single crystal components operating at elevated temperatures are subjected to severe thermomechanical loading conditions. The geometry and behaviour of ...

Evaluation of thermo-mechanical fatigue crack propagation behavior ...

Evaluation of thermo-mechanical fatigue crack propagation behavior of Ni-based single crystal superalloy CMSX-4 · Y. Mukai, H. Kagawa, +1 author. M. Okazaki ...

Coating effects on crack growth in a single crystal nickel based alloy ...

Title: Coating effects on crack growth in a single crystal nickel based alloy during thermo-mechanical fatigue. Conference · Tue Dec 31 00:00:00 EST 1996.

Thermo-mechanical fatigue crack growth in a nickel-based powder ...

Moverare J, Reed R. Thermomechanical fatigue in single crystal superalloys. In MATEC web of conferences. 2014;14:06001. https://doi.org/10.1051/matecconf ...

Thermomechanical fatigue crack growth in a cast polycrystalline ...

... TMF crack initiation in single crystal nickel base alloys has been studied extensively [1][2][3][4][5][6][7][8][9][10][11][12][13]. However, less work has ...

Elevated Temperature Fatigue Crack Growth of Single Crystal René ...

Constant-load-amplitude fatigue crack growth tests were conducted at 0.33 Hz over a temperature range of 538 to 871°C for single crystal René N4 nickel bas.

Thermomechanical fatigue crack growth in a cast polycrystalline ...

In- and out-of-phase thermomechanical fatigue of a Ni-based single-crystal superalloy. MATEC Web of Conferences 14, 19003 (2014). Thermomechanical fatigue ...

Thermomechanical fatigue in single crystal superalloys

Rau C Jr, Gemma A, Leverant G. Thermal-Mechanical Fatigue Crack Propagation in Nickel- and Cobalt-Base Superalloys Under Various Strain-Temperature Cycles ...